Copper Nickel Pipes and Tubes | Cupro Nickel Pipes and Tubes

Cupro Nickel Tube 90/10 Tubes | Cupro Nickel Tubes 70/30 Tubes

Importer, Stockholder, Suppliers and Exporter of Cupro Nickel Tubes, Cupro Nickel Pipes and Cupro Nickel Bars in India

Copper Nickel Pipes and Tubes | Cupro Nickel Pipes and Tubes

Cupro Nickel Tubes 90/10

Carbon steel pipes manufacturer & supplierThis form of cupro nickel tubes produced by Tube Tech possess excellent resistance to corrosion by sea water as well as high resistance to erosion corrosion and air-impingement attack. The addition of iron results in 90/10 performing as good as 70/30 in salt water service heat exchangers. These tubes have good strength and ductility at ordinary temperatures and relatively high strength and other mechanical properties at elevated temperatures.

These cupro nickel tubes are widely used in condensers, coolers and heat exchangers where resistance to corrosion and erosion is paramount, yet maintaining a high thermal conductivity rate. To be used preferably in marine conditions. Forms a protective film which is multi-layered in flowing seawater. Resists marine bifouling. 

These cupro nickel tubes are produced in a range of outside diameter, wall thickness various temper conditions to achieve the required mechanical properties and grain size. The mechanical and dimensional characteristics of our products satisfy the most demanding orders that require tight tolerances.

Send enquiry

Cupro Nickel Tubes 70/30

Steber Steel supplies smooth bore 70/30 cupro nickel tubes of the highest standard, rigorously tested to make sure they are suitable for the exacting requirement of condensers and heat exchangers. These cupro nickel tubes have the highest resistance to stress-corrosion cracking. These tubes are available in a variety of outside diameter, wall thickness and tempers to meet the requirement. Superior dimensional control with specified mechanical properties offers trouble free performance and cost saving.

This form of cupro nickel tube gives the best service life under the most adverse conditions because of improved corrosion resistance and almost insensitive to stress corrosion. These cupro nickel tubes are used in heat exchangers where severe erosion and corrosion have been experienced, especially at elevated temperatures, high velocities and extreme turbulence of the circulating media. These cupro nickel tubes have an important bearing not only on the performance of heat exchangers but also on the cost and delivery cycle time of the condenser and heat exchangers where they are used.

Standards

Cupro Nickel Tube90/ 10

Standard

BS2871part3

ASTM B-111

IS 1545

JIS H 3300

NFA 51 102

Symbol

CN 102

C 70600

CuNi10Fe1

C7060

CuNi10Fe1Mn

Cupro Nickel Tubes 70/30

Standard

BS2871part3

ASTM B-111

IS 1545

JIS H 3300

NFA 51 102

NFA 51 102

CN 107

C 71500

CuNi30Mn1Fe

C 7150

CuNi30Mn1Fe


Dimensional Range
Outer Diameter – 4.00 to 22.00 mm
Wall Thickness – Between 0.15mm and 1.50 mm
Length upto 6 mtrs
End Applications

Heat Exchangers, Oil Coolers, Radiators, High Capacity Power Plants, Ship Building & Ship Repairs, Condensers, Offshore Oil rigs, Distiller Tubes, Evaporators, Ferrules etc.

Curpo Nickel Tubes 95/5 & 90/10 for Marine Application

These Cupro Nickel tubes & pipes for Marine application are very important for all Industrial fields. The company has experience in these areas and is able to supply these tubes in accordance with most international standards and special customer requirements.

Chemical Composition

Classi-
fication

Class

Chemical Composition (%)

Related Standards

Cu

Zn

Pb

Fe

P

Sn

Ni

Mn

Al

As

Other

ISS

KS

JIS

ASTM

BS

DIN

Cu-Ni Tube

1

rem.

1.00 max

0.05 max

1.3-1.7

-

-

4.8-6.2

0.3-0.8

-

-

IS:15
45 
CuNi5
Fe

D 5301 C7040

CuNi
95+5 
7040

B 111 
C70400

2871 
CN101

1785 
CuNi
5Fe

2

rem.

1.00 max

0.05 max

1.0-1.8

-

-

9.0-11.0

1.0-max

-

-

IS:15
45 CuNi
10Fe1

C 7060

CuNi
90:10
C 7060


70600

CN102

CuNi
10Fe

Mechanical Properties

Classi-
fication

Temper

Designation

Cu Alloy
UNS No.

Tensile Test

Outside diameter (mm)

Thickness (mm)

Tensile Strength Kgf/mm2

Elongation (%)

Yield Strength (kg/mm2)

Copper Nickel Tube

061

Annealed

C70400

5-250mm

0.8-10

27(260)

9(85)

H55

Light Drawn

C70400

5-250mm

0.8-10

28(275)

-

21(205)

061

Annealed

C70600

5-250mm

0.8-10

28(275)

-

11(105)

H55

Light Drawn

C70600

5-250mm

0.8-10

32(310)

-

25(240)

Cupro Nickel Tubes 90/10 for Heat Exchangers & Condensers

These Cupro Nickel tubes & pipes for Heat Exchangers & Condensers are very important for all Industrial fields. The company has experience in these areas and is able to supply these tubes in accordance with most international standards and special customer requirements. 

Cupro Nickel Tubes 90/10 for Automobile Industries

The Move To Copper-Nickel Tubing

Copper had been proved since the early days to have many good attributes. It was easy to bend and had very high corrosion resistance, but there was concern about its low corrosion-fatigue strength. When copper-nickel was introduced, it displayed corrosion resistance similar to copper, higher general strength and better fatigue strength. Good formability allows ease of flaring and bending, and although the metal cost is greater than that of steel alternatives, copper-nickel is very attractive in view of its extra life, trouble-free installation and safety/reliability characteristics. 

Properties of Copper-Nickel Brake Tubing

The copper-nickel alloy used for brake tubing typically contains 10% nickel, with iron and manganese additions of 1.4% and 0.8% respectively. The product conforms to ASTM B466 (American Society for Testing and Materials), which specifies dimensions, tensile strength and yield strength. Formability and internal cleanliness conform to specifications SAE J527, ASTM A254 and SMMT C5B (Society of Motor Manufacturers and Traders). Also, the alloy meets the requirements for pressure containment, fabrication and corrosion resistance for ISO 4038 (International Standards Organization) and SAE J1047.

Dimension Tolerance

Material

Ultimate Tensile Strength1000 psi (MPa)

Yield Strength 0.5% Ext.under Load 1000 psi (MPa)

YElongation % in 2 in.

Fatigue Strength (10×7 cycles) 1000 psi (MPa)

Burst Pressure* 1000 psi (MPa)

Copper-brazed Steel

48-55 (0.330-0.380)

28-34 (0.190-0.235)

30-40

30 (
0.210)

19.5 
(0.135)

C12200-Phosphorus deoxidized Copper

32-38 (0.220-0.265)

10-14 (0.070-0.100)

45-60

10 
(0.070)

12 (
0.083)

C70600-Copper Nickel 90-10

48-54 (0.330-0.370)

16-22 (0.110-0.150)

40-55

15 
(0.100)

19 (
0.130)

Alloy C70600 is normally supplied as redrawn tubing in the annealed condition. The combination of strength and good ductility give excellent formability. 
As copper-nickel is softer than steel, it was first feared that fretting might be a problem. Experience has shown this is not the case.

Corrosion Resistance
For many years prior to its application as a brake tubing material, alloy C70600 had been used in ships, power station condensers and hydraulic lines on tankers, and had displayed excellent resistance to saline conditions. Early tests revealed that copper-nickel has almost the same resistance to burst pressure as steel. In testing, however, when exposed to salt spray over 180 days, steel’s burst strength decreases significantly. The copper alloy remains consistently resistant.
For tubes covered with a moist, salty mudpack for six months, brazed steel was severely corroded resulting in perforation of the tubing wall; whereas, only superficial general corrosion was found on the copper-nickel tubing. ISO 4038 and SAE J1047 include a corrosion resistance requirement referring to ISO 3768 asking for a minimum burst pressure of 110 MPa after 96 hours in neutral salt spray. Swedish requirements include a resistance at least equal to 25µ of zinc. In all cases alloy C70600 easily exceeds the required corrosion resistance.

Copper-nickel brake tubing provides superior reliability and assures both manufacturers and vehicle owners improved durability for effective long-life functioning of the brake system.

Cupro Nickel Rods 90/10 and 95/5

Cupro Nickel Rods For 90/10 Cupro Nickel Rods For 95/5

Chemical Properties

Pb

0.05 Max.

Fe

1.00 – 1.80

Mn

1.00 Max.

Zn

1.00 Max.

Cu + Ag Remainder Ni + Co 9.00 – 11.00

Mechenical Properties
Light Drawn

Flattening Test

Reqd. (After ‘O’)

U.T.S. ksi

45.00 Min

Y.S. at 0.5% Ext. ksi

35.00 Min.

Expansion Test 30% at 60 degree Reqd. (After ‘O’)

Annealed Temper

Flattening Test

Reqd.

Grain Size at 75 X mm Avg.

0.010 – 0.045

U.T.S. ksi

40.00 Min.

Y.S. at 0.5% Ext. ksi

15.00 Min.

Expansion Test 30% at 60 degree Reqd.

Chemical Properties

Sn

0.10 Max.

Pb

0.05 Max

Ni

4.00 – 5.00

Fe

0.10 Max.

Mn

0.25 Max.

As

0.10 Max.

Cu + Ag

95.00 – 96.000

Sb

0.01 Max.

Bi

0.0025 Max.

Oxygen (O2) 0.08 Max.

Mechenical Properties
Annealed

U.T.S. MPa

216 – 275 (Strip cut from Ring Tube)

%Elongation at 5.65Sq.Rt So G.L.

40.00 Min. (Strip cut from Ring Tube)

Flattening Test

Reqd.

Bend Test

Reqd. (180 degree close)

Cupro Nickel Pancake Coils

Copper-nickel brake tubing provides superior reliability and assures both manufacturers and vehicle owners improved durability for effective long-life functioning of the brake system.Coils Available in 5 mtr, 10 mtr & 15mtrs.

Contact Steber Steel today for a Copper Nickel Pipes and Tubes competitive quotation…
call : (+91) 22-23824442
e-mail: sales@stebersteel.net

Copper Nickel Pipes and Tubes, best quality Copper Nickel Pipes and Tubes, wide variety of Copper Nickel Pipes and Tubes, Copper Nickel Pipes and Tubes India, Copper Nickel Pipes and Tubes distributor Mumbai, Copper Nickel Pipes and Tubes traders, prime quality Copper Nickel Pipes and Tubes, Source for Copper Nickel Pipes and Tubes, specialize in Copper Nickel Pipes and Tubes, Copper Nickel Pipes and Tubes with Test Certificate IBR Certified